The potential of electrospun pullulan/dextran (P/D) nanofibers (average diameter = 323 nm) for vascular tissue engineering applications is explored. The mechanical properties of the nanofibers are of the same order of magnitude as that of human arteries (Young's modulus approximate to 0.88 MPa; tensile strength approximate to 0.35 MPa). It is demonstrated that the nanofiber topography enables cell adhesion and that the endothelial phenotype is maintained on the nanofibers. Moreover, P/D nanofibers support a stable confluent monolayer of endothelial cells over 14 d. SMCs seeded on nanofibers display similar levels of alpha smooth muscle actin and a lower proliferation rate than cells on 2D cultures. The observations suggest that nanofibers promote a shift to a quiescent contractile phenotype in SMCs.