Titania (TiO(2)) nanofibers and composite thin films of titania nanofibers and Safranin O dye (SAF) were studied. TiO(2) nanofibers were prepared by electrospinning technique from titanium tetra-isopropoxide precursor solution in ethanol. Surface topology of the nanofibers was observed using scanning electron microscopy (SEM), their crystal structure was studied by X-ray diffraction (XRD) and the chemical composition by X-ray photoelectron spectroscopy (XPS). Properties of the TiO(2) nanofibers were studied in dependence on the values of relative air humidity in the range from 15% to 55%. It was necessary to maintain the relative humidity lower than 30% during electrospinning in order to obtain high quality nanofiber films. The average minimum diameter of the as-prepared TiO(2) nanofibers was found to be around 100 nm. Nanofiber diameter diminishes to about 50 nm after annealing at 420 degrees C for 1 h. The as-prepared titania nanofiber films were completely amorphous while anatase crystal phase was detected in the films after annealing. In order to prepare the composite films, solution of SAF dye with poly(vinylpyrrolidone) in ethanol/water was dropped off on the prepared titania nanofibers surface. Opto-electrical properties of SAF dye and the resulting nanocomposite films were studied by UV-Vis spectroscopy and current-voltage characteristics. Safranin O is characterized by two strong absorption peaks: one at 274 nm and a wide band with splitting between 420 nm and 600 nm. The optical energy band gap of titania nanofibers was estimated from the UV-Vis measurements to be 3.4 eV. The charge transport in the composite films is influenced by the space charge limited currents due to the very high resistance of the materials. (C) 2010 Elsevier B.V. All rights reserved.